Flexible, Thin Wall Flame Retardant Polyolefin Tubing Shrink Ratio
December 16, 2016
Zero Halogen, Flexible Flame Retardant Heat Shrinkable Tubing
December 21, 2016Heat Shrinkable End Caps With Spiral Adhesive Coating

Product Description
The Heat Shrinkable End Caps with Spiral Adhesive Coating offers an economical means of sealing the end power cable with perfect watertight seal. The internal surface of the end cap has a layer of spiral coated hot melt adhesive, which retains its flexible properties after recovery. HSEC is recommended for applications both in open air and underground power distribution cables with PVC, Lead or XLPE sheaths. Cable end caps with the spiral adhesive coating. Effectively offering protection against oxidation, ozone, UV-radiation etc. Coated with conductive mastic to environmental seal. Easily to fit into the cable end. Minimum fully shrink temperature of 120°C.
Features:
- Crosslinked Polyolefin
- Excellent Sealing Properties
- UV & Weather Resistance
- Operating Temp: -55°C to +110°C
- Min. Shrink Temp. : 120°C
- Available With or Without Adhesive
Technical Properties:
Property | Test Method | Typical Data |
---|---|---|
Tensile Strength | ASTM D 638 | > 11MPa |
Ultimate Elongation | ASTM D 638 | > 400% |
Density | ASTM D 792 | 1.05g/cm3 |
Ultimate Elongation After Aging | 150°C, 168hrs | > 300% |
Dielectric Strength | IEC 243 | > 15kV/mm |
Volume Resistance | IEC 93 | > 1014Ω CM |
Product Dimensions (mm)
Item Code | As supplied(mm) | After recovered(mm) | Cable Diameter Range (mm) |
---|---|---|---|
D* Internal Diameter (Min.) | d* Internal Diameter (±10%) | ||
DSSB-EC-HSEC145 | 14 | 5 | 5 - 12 |
DSSB-EC-HSEC 2585 | 25 | 8.5 | 10 - 23 |
DSSB-EC-HSEC 3516 | 35 | 16 | 18 - 32 |
DSSB-EC-HSEC 5526 | 55 | 26 | 28 - 48 |
DSSB-EC-HSEC 7536 | 75 | 36 | 45 - 70 |
DSSB-EC-HSEC 10052 | 100 | 52 | 55 - 90 |
DSSB-EC-HSEC 12060 | 120 | 60 | 65 - 110 |
DSSB-EC-HSEC 16082 | 160 | 82 | 80 - 150 |
DSSB-EC-HSEC 20090 | 200 | 90 | 160 - 190 |