Product Description
OVERVIEW
Legend™ LHLZ heatshrink is manufactured to offer a consistently high-grade heatshrink solution. It has a 2:1 shrink ratio. It is made up of Polyolefin Material, compliant to RoHS.
COLOUR OPTIONS
Yellow and White.
Test | Method |
---|---|
Flame Retardant | UL224 |
Fire Testing of Materials and Components for Trains - Oxygen Index & Flue Gas Density | EN 45545-2 |
Technical Information
- Material : Halogen free flame retardant single wall matt printable polyolefin
- Shrink Ration : 2:1
- Minimum Shrink Temperature : 115°C ( 239°F) – fully recovered
- Operating Temperature : -40°C to +105°C (-40°F to 221°F)
- Diaeletic Strength : ≥ 20 kV/mm
- RoHS : RoHS Complaint
- Printing : Silver Fox DTP-1 thermal printer
- Ribbon : TSR3/300/60
- Network Rail : Authorised for Use
Legend™ LSZH Heatshrink
Item Code | Cable OD Ø Exp. (mm) | Cable OD Ø rec. (mm) | Roll Length (m) | Colour |
---|---|---|---|---|
DSSB-CIA-LHLZ/C/R/2.4-1.2T(PF)Y | 2.4 | 1.2 | 16 | Yellow |
DSSB-CIA-LHLZ/C/R/2.4-1.2T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/3.2-1.6T(PF)Y | 3.2 | 1.6 | Yellow | |
DSSB-CIA-LHLZ/C/R/3.2-1.6T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/4.8-2.4T(PF)Y | 4.8 | 2.4 | Yellow | |
DSSB-CIA-LHLZ/C/R/4.8-2.4T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/6.4-3.2T(PF)Y | 6.4 | 3.2 | Yellow | |
DSSB-CIA-LHLZ/C/R/6.4-3.2T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/9.5-4.8T(PF)Y | 9.5 | 4.8 | 14 | Yellow |
DSSB-CIA-LHLZ/C/R/9.5-4.8T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/12.7-6.4T(PF)Y | 12.7 | 6.4 | Yellow | |
DSSB-CIA-LHLZ/C/R/12.7-6.4T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/19.1-9.5T(PF)Y | 19.1 | 9.5 | 12 | Yellow |
DSSB-CIA-LHLZ/C/R/19.1-9.5T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/25.4-12.7T(PF)Y | 25.4 | 12.7 | Yellow | |
DSSB-CIA-LHLZ/C/R/25.4-12.7T(PF)W | White | |||
DSSB-CIA-LHLZ/C/R/38.1-19.1T(PF)Y | 38.1 | 19.1 | 11 | Yellow |
DSSB-CIA-LHLZ/C/R/38.1-19.1T(PF)W | White | |||